Physical degradation of CD's


Hello friends,

Please keep in mind that I am new to the digital world and I'm just curious about something....

I have just recently bought two Dac's.  As I've been trying to break them in, I've had a cd player spinning a cd 24/7 on repeat into the dac.

I'm wondering, does the cd laser constantly going over the same pits over and over again, somehow degrade the physical aspect of the cd layer that is being read by the laser?

I know that I wouldn't want to replay my precious vinyl over and over again, but in that case I'm physically dragging a diamond stylus through the record grooves.  

I have no idea if the laser does anything to the bits it's trying to read when kept on 24/7?

Thank you and best wishes to you all,

Don

no_regrets

A Japanese 100V unit works just fine in the US.. I bought the CEC TL-5....talked to an electrician....said it would be fine...It's better than fine.

Post removed 

I own thousands of discs . I had a few early CDs, and several CDRs, that bronzed, but they play and I still listen to them .  The few CDs that I thought might have deteriorated all were cured with a good cleaning 

Many years ago, when I was a contributing editor to various mainstream tech publications, I did a large feature on disc rot. Spoke at length with engineers, large manufacturing & fab facilities, the whole nine yards. At this point, I don’t remember where it was published, maybe PC Magazine.

The bottom line is that "CD rot" today is pretty friggin’ unlikely. There were reports that the first generation of CDs were subject to this problem, and it was eventually traced back to a single disc-fab plant, I think in Europe, that was a source for discs worldwide. The issue was an improper seal that allowed air to contact the aluminum layer, causing black oxidation. This, of course, changed the reflectivity of the pits & lands, making parts of the disc unreadable. Most people I spoke with believed that this happened only when the disc was flexed or otherwise abused to the point of breaking the original seal. My conclusion was that this was an exceedingly rare occurrence, very much overplayed in the press.

Note that I’m talking about replicated discs. Home-recorded recordable CDs, for some reason, are much more susceptible to this problem. But again, it seems as though the issue was mostly with earlier generations of recordable media and, even in worst case, it would take years to manifest. Much more common than silver-disc "rot", but still pretty rare. My personal opinion (and it's just an opinion, not something I can verify) is that the greater number of problems with recordable CDs has more to do with the fact that they use potentially degradable photoreactive inks.  But at this point, who knows?

This shouldn’t be confused with "DVD rot," which was technically similar, but much more common. DVDs are composed of multiple layers of plastic glued together, and are thicker. In terms of physical structure, they’re more susceptible to damage by flexing. This problem was exacerbated by early DVD jewel cases, which made it more likely that unthinking users would flex the heck out of a disc while trying to pry it out of the case.

Again, this was a problem related to early manufacturing issues, that were later worked out. And although more common than "CD rot", which borders on urban legend, it was still pretty rare.

I have examples of "rotted" discs still sitting on a shelf somewhere. If I get the chance, I’ll take some pictures & post them here so you can see what "rot" looks like.